Home > Products > Dental Zirconia Blocks > Multilayer Zirconia Blocks > UT Multilayer Zirconia Blocks

  • UT Multilayer Zirconia Blocks

  • UT Multilayer Zirconia Blocks

  • UT Multilayer Zirconia Blocks

  • UT Multilayer Zirconia Blocks

UT Multilayer Zirconia Blocks

Attribute

The characteristics: 6 layers color gradient, 49% translucency; Strength ≥800Mpa

Color: A1/A2/A3/A3.5/A4, B1/B2/B3/B4, C1/C2/C3/C4, D2/D3/D4, OM1/OM2/OM3

Size: 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm

Indications 1: inlay, onlay, posterior crown

Indications 2: veneer, anterior crown, anterior crown bridge(up to 3 units)

Product Description

Product Description

HaHasmile® UT Multilayer Zirconia Blocks is most translucent Multilayer zirconia blocks, UT Multilayer Zirconia Blocks can make anterior teeth.

 

Our advantage prices

As we are direct manufacturer for more than 10 years zirconia blocks experience, our zirconia blocks have very high quality, monthly output 60000pcs. In order to give more benefit to our customers,  we just have cost prices. 12mm-25mm the prices is $55-$85/pcs.

 

UT Multilayer zirconia blocks

12mm

14mm

16mm

18mm

20mm

22mm

25mm

$55.00

$60.00

$65.00

70.00

$75.00

$80.00

$85.00

UT Multilayer Zirconia Blocks

HaHasmile® UT Multilayer Zirconia Blocks Features:

6 layers gradient multilayer colors;

Very high translucent 49%;

Bending Strength 800Mpa;

Suitable for anteior teeth, crown, 3 units bridge;

HaHasmile® UT Multilayer Zirconia Blocks has color gradient.

Available for 98mm/95mm

Thickness: 12mm / 14mm / 16mm / 18mm / 20mm / 22mm / 25mm

Color: A1 / A2 / A3 / A3.5 / A4 / B1 / B2 / B3 / B4 / C1 / C2 / C3 / C4 / D2 / D3 / D4 / OM1 / OM2 / OM3

 

HaHasmile® UT Multilayer zirconia blocks are produced by CIP technology and pre-sintered in low temperature. Although the product has some strength, because of porosity, please handle carefully.

UT Multilayer Zirconia Blocks

UT Multilayer zirconia blocks materials function:

The zirconia can be used to manufacture crown bridges and other restoration.

 

Chemical Composition

Components UT Multilayer Zirconia block
Nanometer zirconia powder ≥98%
CeO₂ <0.5%
Fe2O3 <0.5%
Er2O3 <0.5%
Other Oxides <0.5%

 

UT Multilayer zirconia block Mechanical Property

Sintered Density g/cm³ >6.02g/cm³
Bending Strength Mpa ≥800Mpa
Translucency 49%
Hardness(Hv10) 1250MPa
Sintered temperature(°C) 1500°C
Radioactivity Bq.g-1 <0.1
Cytotoxicity Level0

 

Indications:

Veneer, inlay, onlay, anterior crown, anterior crown bridge(up to 3 units), posterior crown.

UT Multilayer Zirconia Blocks

Application Method

Full contour crown and bridges

Scanning — Designing  — Milling — Cleaning — Sintering — Polishing — Staining — Finishing

UT Multilayer Zirconia Blocks

HaHasmile® UT Multilayer Zirconia Block Sintering Curve:

Below and 3 units bridge(10h)

Start temp Heating rate Maximum temp Heating rate Maximum temp Heating rate Maximum temp Heating rate Maximum temp Holding time Cooling rate Cooling to Cooling rate Cooling to
Room temp 10°C/min 300°C 7°C/min 1000°C 5°C/min 1200°C 3°C/min 1500°C 120min 7.3°C/min 800°C Natural 100°C